HIGH STRENGTH EPOXY ADHESIVE epigen 0907


Quantity: In Stock

Category: Adhesives & High Strength Glues

Quick Overview:

Share: Messenger


A tough multipurpose epoxy paste for general adhesive, grouting and caulking applications, for use on a variety of surfaces including steel, concrete, timber and fibreglass. Characterised by exceptional toughness and durability, originally designed for ceramic wear tile bedding and grouting. Uses extend to fairing blowholes on concrete, and pitting on steel surfaces prior to coating. Can be sanded or machined to shape or tolerances.
 
Epigen 907 possesses excellent water resistance and resists many chemicals including degreasers, cleaners, aviation fuels and lubricants, acid and alkali reagents.
 

TYPICAL APPLICATIONS

  • Ceramic Tile Adhesive
  • Fairing Fibreglass and Bonding Fabrications
  • Applying Fillets and Aris to Steel or Concrete Surfaces
  • Fairing Pitting or Holes on Steel and Concrete
  • Chemical Anchor & Rock Bolt Adhesive
  • Grouting Reinforcement Bars
  • Concrete Crack and Void Repair
  • Grout for Swages

FEATURES
 
  • Resistant to a variety of chemicals
  • Food industry suitable
  • Non sag viscosity for easy installation
  • Free of all solvents - zero VOC
  • Tough and durable
  • Versatility in application allows concrete patching
  • Suitable on steel to void fill or fair surfaces
  • Strongly adhesive for optimum adhesion
Epigen 907 is supplied as a two part kit comprising component “A” resin, and component “B” curative.
The entire kit is supplied in a pre weighed convenient size to make on site activities easier.
 
Peerless Industrial Systems can provide information on specific applications based on industry acceptable practices or historical results.]


PROFILE        
Colour Off White      
Ratio by weight 1 kg Component “A”    
  0.5 kg Component “B”
Pot Life minutes @ 24oC 30      
Mixed consistency @ 24oC Paste       
Specific gravity when mixed 1.4      
Coverage /m 2 @ 10mm 14.0 kg      
         

TYPICAL CURED PROPERTIES  
Compressive strength ASTM D695, Mpa 72
Tensile strength ASTM D638, Mpa 16
Flexural strength ASTM D790, Mpa 32
Hardness, Shore D >82
Elongation ASTM D638, % 1.3
Tensile Adhesion ASTM 4541, MPa >12 
Thermal conductivity ASTM C177, Kcal/m.hro C 0.6
Coeff of Therm Exp ASTM C531, 10-5/o C 1.9
Maximum exposure temperature, o C 110
Heat deflection temperature ASTM D648,  o C 70
Thin Film Gel @ 12mm, Minutes 60
Thin Film Set @ 12mm, Minutes 120
Ultimate cure time, Hours 96
   
This information is supplied as an indicative reference only. Caution should be used where direct comparisons with other products are to be made.

SURFACE PREPARATION                                                                
                                                                       
                                                                       
Methods for surface preparation prior to use include using chemical means such as washing & etching, high pressure water blasting, or mechanical techniques such as abrasive blasting, grinding or scarifying.                                
Specialist advice is available from Peerless Industrial Systems to ensure the correct preparation procedure is employed for specific application.                                            
APPLICATION                                                                  
                                                                       
                                                                       
Mixing of product should be carried out using spatula or by slow speed blender, and completed by adding to the component “A”, component “B”. Ensure the mixed 907 is homogenous and the final colour shall be an even grey without streaks.                          
Bedding:                                                                    
                                                                       
                                                                       
In all cases, the depth nominally 2mm minimum should be used to ensure sufficent adhesive is in place and afford reasonable compressive strength. There is no maximum thickness requirement. No primer is required to facilite adhesion unless the surface is loose or friable. In cool environments, pre warm the product before use.          
Adhesive Applications:                                                                  
Apply a thin coat of Epigen 907 to both surfaces before bringing the two together. Do not use where a flexible or resilient glue line is required. Recommended where a tough and strong, or heavy shock resistant material is required (eg: Ceramic Tiles to Steel on chutes, steel onto steel, concrete onto steel). Preheat the material before use to achieve best cure rate and strength when cold.

 


COVERAGE GUIDE      
Bedding Application - nominally 5mm thickness
         
7kg = 1000mm X 1000mm X 5mm  
         
Bulk Filling Application     
         
1.4kg = 1 litre      
         
1.4kg = 100mm X 100mm X 100mm  

CHEMICAL RESISTANCE

Tested at 21oC. Samples cured for 10 days at 25oC. Curing at elevated temperatures will improve chemical resistance.
 
1 = Continuous or long term immersion
2 = Short term immersion

3 = Splash and spills
4 = Avoid contact

Acetic Acid, 10 %    2 Acetone 2
Acetic Acid, Glacial    2 Ammonium Chloride 1
Hydrochloric Acid, 5 %    1 Beer 1
Hydrochloric Acid, 10 %    2 Dichloromethane 4
Hydrochloric Acid, conc    2 Diesel Fuel 1
Nitric Acid, 5 %                         2      Isopropyl Alcohol              2
Nitric Acid, 10 %                       2      Kerosene                            1

Phosphoric Acid, 5 % 1 Petrol 2
Phosphoric Acid, 20 % 2 Salt Water 1
Sulfuric Acid, 5 % 3 Sewage 2
Sulfuric Acid, 20 % 3 Skydrol 2
Ammonium Hydroxide, 5 % 1 Sodium Cyanide 1
Ammonium Hydroxide, 20 % 1 Sodium Hypochlorite 2
Potassium Hydroxide, 5 % 1 Toluene 2
Potassium Hydroxide, 20 % 1 Trichloroethane 3
Sodium Hydroxide, 5 % 1 Wine 2
Sodium Hydroxide, 20 % 1 Xylene 2
           

CURE
Variations in cure may arise due to the amount of material being applied, the thickness of material being applied, the surface temperature, and the product temperature. The cure may be increased by heating product or by leaving mixed material stand for 15 minutes before use. The cure may be decreased by cooling the product before mixing


 


Sorry, Currently No Video Uploaded.
Sorry, Currently No File Uploaded.

HIGH STRENGTH EPOXY ADHESIVE epigen 0907


Please Leave Your Product Enquiry Here. We will Get Back To You Soon.😳

Product Specifications

  • Product SKU : -
  • Weight (GRAM) : -
  • Dimension : -

Locate Us