A tough infusible solvent free epoxy resin based system designed for use as a multipurpose high strength casting and grouting polymer and 'wet to dry' concrete adhesive. It may be applied by either roller or brush.
This product is designed to be used effectively on wet or dry concrete, in hot or cold climates.                    

Wet to Dry Concrete Adhesive  
Bedding Rails & Tracks  
Floor Re Levelling & Crack Repair 
High Strength Adhesive  
Casting Mould Making   
Chemical Anchoring    

  • Engineered for high mechanical strength
  • Extremely strong adhesive
  • Broad spectrum chemical resistance
  • Cures in 6 hours
  • Free of all solvents - zero VOC
  • Cures even when applied under cold adverse conditions
  • Suitable for underwater use

ASTM C882 - 65 MPa Base / 65 MPa Scarf Joint Bond Strength reported in MPa.
Smooth Saw Cut
Dry                                                              52
Wet                                                    14

Rough Exposed Aggregate Dry           49
Wet                                                    18

Ratio by weight   2 parts Component “A” 
      1 part Component “B”
Pot Life minutes @ 24oC   30  
Mixed consistency @ 24oC  Flowable Liquid
Specific gravity when mixed 1.3  

Compressive strength ASTM D695, Mpa  Flexural strength ASTM D638, Mpa  >90
Tensile strength ASTM D638, Mpa         >21
Flexural strength ASTM D638, Mpa         >21
Hardness, Shore D           88
Comp Modulus of Elasticity ASTM D695, Mpa        >1200
Elongation D638           2.60%
Coefficient of thermal expansion ASTM C531 (cm/cm/o C) x 10-5     3.7
Dielectric constant ASTM D150 (150KHz)       3
 Maximum exposure temperature, o C         130
Heat deflection temperature ASTM D648, o C       75
Cure time @ 20mm, Minutes         90
Cure time to open service @ 20mm, Hours        4
Ultimate cure time @ 20mm, Hours         48


Methods for substrate preparation preference using high pressure water blasting, or mechanical techniques such as grinding or scarifying.
Specialist advice is available to ensure suitable preparation procedure is employed for specific applications.


Mixing of product should be carried out using slow speed mixers and carried out by adding component “B” to the component “A”. Once uniform in colour, mixed product should be poured directly into the area requiring treatment or applied to surfaces nominated for service using a brush or roller.
When filling large cavities, Epigen 1009 may be bulk filled with equal parts by weight 16/30 mesh Silica Sand to reduce the amount of resin used. This is seen as an advantage particularly with high ambient temperature since the addition of aggregate reduces the exotherm and any resultant post cure contraction. The addition at the recommended rate will retain strength and pourability features.


In grouting applications, waxed timber, acrylic sheet, mild steel or galvanised forms have also be used with equal success.
Seal joins using silicon sealant.                

The following results represent relevance when in grouting applications of chemical facilities.
Tested at 21oC. Samples cured for 10 days at 25oC.
1 = Continuous or long term immersion

2 = Short term immersion
3 = Splash and spills
4 = Avoid contact

Acetic Acid, 10 % 2 Ammonium Chloride 1
Hydrochloric Acid, 5 % 1 Beer 1
Hydrochloric Acid, 10 % 1 Dichloromethane 4
Hydrochloric Acid, conc 2 Diesel Fuel 1
Nitric Acid, 10 % 2 Kerosene 1
Phosphoric Acid, 5 % 1 Petrol 1
Phosphoric Acid, 20 % 2 Salt Water 1
Sulfuric Acid, 5 % 2 Sewage 1
Sulfuric Acid, 20 % 3 Skydrol 1
Ammonium Hydroxide, 5 % 1 Sodium Cyanide 1
Ammonium Hydroxide, 20 % 1 Sodium Hypochlorite 1
Potassium Hydroxide, 5 % 1 Toluene 2
Potassium Hydroxide, 20 % 1 Trichloroethane 2
Sodium Hydroxide, 5 % 1 Wine 1
Sodium Hydroxide, 20 % 1 Xylene 1


Variations in cure may arise due to the amount of material being applied, the thickness of material being applied, the surface temperature, and the product temperature. The cure may be increased by heating product or by leaving mixed material stand for 15 minutes before use. The cure may be decreased by cooling the product before mixing.

Sorry, Currently No Video Uploaded.
Sorry, Currently No File Uploaded.


Please Leave Your Product Enquiry Here. We will Get Back To You Soon.😳

Product Specifications

  • Product SKU : -
  • Weight (GRAM) : -
  • Dimension : -

Locate Us