FASTPATCH ADHESIVE epigen FC3


Quantity: In Stock

Category: Adhesives & High Strength Glues

Quick Overview:

A fast curing patching paste for repairing holes, cracks and gaps, characterized by the fibre reinforcement that allows voids to be bridged adding structural strength. Bonds to a variety of surfaces including steel, plastics, timber and fibreglass.
 
Extremely tough, it cures quickly to form a hard infusible plastic that resists impact and cracking.
 
Epigen FC3 possesses excellent water resistance and resists many harsh and aggresive chemicals including degreasers, cleaners, aviation fuels and lubricants, acid and alkali reagents.


TYPICAL APPLICATIONS

  • Pump and Cyclone Repairs
  • Pipe and Elbow patching
  • Sealing Oil Transformers
  • Patching holes in boats
  • Water pipe repair
  • Tank patching

FEATURES
  •  Fibre reinforced for strength 
  • Resistant to a variety of alkali & acids
  • Food industry suitable
  • Non sag viscosity for easy installation
  • Free of all solvents - zero VOC
  • Tough and durable
  • Suitable on steel to patch all breaks and gaps
  • Exhibits strong adhesive to plastics including PVC

Epigen FC3 is supplied as a two part kit comprising component “A” resin, and component “B” curative.
The entire kit is supplied in a pre weighed convenient size to make on site activities easier.
 
Peerless Industrial Systems can provide information on specific applications based on industry acceptable practices or historical results.


PROFILE        
Colour Green      
         
Ratio by weight 1 kg Component “A”    
  0.5 kg Component “B”
Pot Life minutes @ 24oC 15      
Mixed consistency @ 24oC Paste       
Specific gravity when mixed 1.4      
Coverage /m 2 @ 10mm 14.0 kg      
TYPICAL CURED PROPERTIES

Compressive strength ASTM D695, Mpa 82
Tensile strength ASTM D638, Mpa 24
Flexural strength ASTM D790, Mpa 36
Hardness, Shore D >85
Elongation ASTM D638, % 0.7
Tensile Adhesion ASTM 4541, MPa >14
Thermal conductivity ASTM C177, Kcal/m.hroC 0.6
Coeff of Therm Exp ASTM C531, 10-5/C 1.5
Maximum exposure temperature, C 120
Heat deflection temperature ASTM D648, C 80
Thin Film Gel @ 6mm, Minutes 15
Thin Film Set @ 6mm, Minutes 30
Ultimate cure time, Hours 18

SURFACE PREPARATION

Methods for surface preparation prior to use include using chemical means such as washing & etching, high pressure water blasting, or mechanical techniques such as abrasive blasting, grinding or scarifying.
Specialist advice is available from Peerless Industrial Systems to ensure the correct preparation procedure is employed for specific application.

APPLICATION

Mixing of product should be carried out using spatula, and completed by blending the component “A” with component “B”. Ensure the mix is homogenous and free from lumps. The final colour shall be even green without streaks.
Smear a thin coat of Epigen FC3 to all surfaces before overlaying the paste across the entre area to complete the treatment. Do not use where a flexible or resilient glue line is required. Recommended where a tough and strong, or heavy shock resistant material is required.
In large voids, two applications may be applied to bridge the gap or lay a stick or rod to aid support of the Epigen FC3. During cure, exotherm can build up to cause sag.

 
CHEMICAL RESISTANCE

Tested at 21oC. Samples cured for 10 days at 25oC. Curing at elevated temperatures will improve chemical resistance.
 
1 = Continuous or long term immersion
2 = Short term immersion
3 = Splash and spills
4 = Avoid contact
                 

Acetic Acid, 10 % 1 Acetone 2
Acetic Acid, Glacial 2 Ammonium Chloride 1
Hydrochloric Acid, 5 % 1 Beer 1
Hydrochloric Acid, 10 % 2 Dichloromethane 4
Hydrochloric Acid, conc 2 Diesel Fuel 1
Nitric Acid, 5 %  2 Isopropyl Alcohol 1
Nitric Acid, 10 % 2 Kerosene 1
Phosphoric Acid, 5 % 1 Petrol 1
Phosphoric Acid, 20 % 2 Salt Water 1
Sulfuric Acid, 5 % 3 Sewage 2
Sulfuric Acid, 20 % 3 Skydrol 2
Ammonium Hydroxide, 5 % 1 Sodium Cyanide 1
Ammonium Hydroxide, 20 % 1 Sodium Hypochlorite 2
Potassium Hydroxide, 5 % 1 Toluene 2
Potassium Hydroxide, 20 % 1 Trichloroethane 3
Sodium Hydroxide, 5 % 1 Wine 1
Sodium Hydroxide, 20 % 1 Xylene 2

CURE
Variations in cure may arise due to the amount of material being applied, the thickness of material being applied, the surface temperature, and the product temperature. The cure may be increased by heating product or by leavingmixed material stand for 15 minutes before use. The cure may be decreased by cooling the product before mixing.

Share: Messenger


 



 




 


Sorry, Currently No Video Uploaded.
Sorry, Currently No File Uploaded.

FASTPATCH ADHESIVE epigen FC3


Please Leave Your Product Enquiry Here. We will Get Back To You Soon.

Product Specifications

  • Product SKU : -
  • Weight (GRAM) : -
  • Dimension : -

Locate Us